Boron Carbide Plate
18- 碳化硼板
- Boron Carbide Plate
- B4C; 95%
- 30*30*9; 245*295*10; 17*48; 250*300; 200*250; 150*200; 150x150mm
- 2.51
- 2.28
- High wear-resistant nozzle, high-precision sealing ring, aerospace vehicle surface coating, military bulletproof armor, etc
- 产品详情-Products Details
Boron Carbide (B4C) ; Molecular Weight: 55.26
Form : Black or Dark Gray Plate
Boron carbide is an inorganic non-metallic high-performance structural ceramic material formed by the combination of boron and carbon at high temperature. At the same time, it also has functional ceramic properties. It is rhombohedral under microscopic observation. It is one of the hardest man-made materials. Its hardness is second only to diamond and cubic boron nitride.
Mohs hardness:9.36; Microhardness: 5400-6300kg/mm ²， Specific gravity 2.52g/cm ³， Melting point 2450 ℃, high temperature resistance, no chemical reaction with acid and alkali.
It has the characteristics of stable chemical properties, light weight, high hardness, semiconductor and so on.
Due to its high hardness, it is suitable for grinding, polishing, drilling and other processing of various cemented carbide, gem and other materials, and manufacturing engineering ceramic abrasives, precision measuring elements and engineering ceramic products with high wear resistance, such as high wear-resistant nozzles for aeroengines, high-precision sealing rings, surface coatings of aerospace vehicles, military bulletproof armor sheets, etc, Because the boron contained in it has the characteristics of thermal neutron absorption cross section and high boron content, it is the main boron containing material for the manufacturing of reaction rate regulating rod in nuclear industrial reactor.
Advantage:1. High heat resistance2. Wear resistance3. Corrosion resistance4. High bending strength5. Low density and light weight6. Custom shapes
Boron carbide ceramics
Performance | Unit | Value |
Bending strength | MPa | ≥310 |
Compressive strength | MPa | ≥2000 |
Elastic modulus | GPa | ≥380 |
Vickers hardness | GPa | ≥30 |
Density | g/cm3 | ≥2.48 |
Apparent porosity | % | ≤0.1 |
Fracture Toughness | MPa·m1/2 | ≥4.30 |
Boron carbide bulletproof ceramics
Name | Boron carbide bulletproof plate |
Material | Boron carbide ceramics+PE(Kevlar) |
Shape | Flat; Single curved |
Size | 250X300mm; 200x250mm; 150x200mm;150x150mm |
Resistance bullet type | 5.8mmbullet |
Protection class | GA 6 |
Boron carbide nuclear power protective ceramics
Density (g/cm3)) | 1.8-2.4 |
Rockwell hardness (HRA) | ≥70 |
Compressive strength（MPA） | ≥700 |